Home Industrial Supplies

sunlight l-200

faceboox pinterest twitter share

Negotiable Min Order Quantity Unit

Required Quantity

Place of Origin

Payment Terms: Negotiable

Production method: Negotiable

Shipping / Lead Time: Negotiable / Negotiable

Keyword: sunlight, sunlight l-200, high temperature tape, htt sunlight

Category: Industrial Supplies

SEND TO SUPPLIER INQUIRY

Daehyun tech., inc

Membership: PRO

Country / Year Established: South Korea /

Business type: Others

Verified Certificate

DUNS

Minisite Follow Company

PRODUCT DESCRIPTION COMPANY INFORMATION Related Products

Product name	sunlight l-200	Certification	-
Category	Industrial Supplies	Ingredients	-
Keyword	sunlight , sunlight l-200 , high temperature tape , htt sunlight	Unit Size	-
Brand name	-	Unit Weigh	-
origin		Stock	-
Supply type	-	HS code	-

Product Information

1	GENERAL

	FOR TEMPERATURES EXCEEDING 135°C AND UP TO 200°C A FIVE LAYER SYSTEM "SUNLIGHT L-200"
	CONSISTING OF A PRIMER MADE PRINCIPALLY WITH A SILICONE OR PHENOLIC RESIN BINDER AND
	A SPECIALLY PROCESSED TAPE SHALL BE USED.

2	MATERIAL
	MATERIAL TO BE USED ;

	* PRIMER (UNDER COAT)	: SUNLIGHT L-200 PRIMER
	* WRAPPING TAPE	: SUNLIGHT L-200 TAPE
	* MIDDLE COAT	: SUNLIGHT L-200 AC PRIMER
	* FILLING MASTIC	: SUNLIGHT L-200 CEMENT
	* TOP COAT	: SUNLIGHT TOP COAT

2.1	SUNLIGHT L-200 PRIMER (2 LAYERS)

	THE PRIMER OF SUNLIGHT L-200 SYSTEM MADE PRINCIPALLY WITH A SILICON EPOXY RESIN
	BINDER. THIS PRIMER SHALL BE APPLIED BY BRUSH OR ROLLER COATING IN TWO LAYERS AT
	25 MICRONS THICKNESS PER EACH LAYER AND SHALL MEET THE CHARACTERISTICS STATED
	BELOW AND CONFIRM TO COMPANY APPROVED DATE PROVIDED BY THE MANUFACTURER

	BASE	SILICON EPOXY
	DFT (DRY FILM THICKESS)	25 MICRONS (EACH LAYER)
	DRYING TIME	20-30 MINUTES AT 25°C AND 60% OF MOISTURE
	GUIDANCE COVERAGE	0.2 KG/M2 (NET SURFACE)
	SPECIFIC GRAVITY	1.16 (25°C)
	NONVOLATILE COMPONENT	60 +/- 1% WT
	VISCOSITY	8.0 +/- 3 PS (25°C)
	NOTE : INTERVAL OF 1ST COATING AND 2ND COATING REQUIRED MINIMUM 1 HOUR

2.2	L-200 TAPE

	THE L-200 TAPE SHALL HAVE A POLYAMIDE BASE MATERIAL WITH THE CHARACTERISTICS STATED
	BELOW ;

	BASE	POLYAMDE
	IMPREGNATED MATERIAL	TAPE IMPREGNATED WITH SILICONE EPOXY RESIN LIQUID
	THICKNESS (BEFORE APPLICATION)	0.5 mm +/- 0.02 mm
	THICKNESS (AFTER APPLICATION)	0.45 mm =/- 0.02 mm
	MAXIMUM TEMPERATURE	200°C
	WIDTH	50,100 & 150 mm

	APPLICATION METHOD IS WRAPPING MANUALLY, KEEPING ADEQUATE TENSION WITH A 55%mm
	OVERLAP ONTO PIPE SPIRALLY. AS FOR DETAIL THE APPLICATION MANUAL OF MANUFACTURER
	SHALL BE CONSIDERED.


2.3	L-200 AC PRIMER

	AFTER THE SUNLIGHT L-200 TAPE HAS BEEN APPLIED, L-200 AC PRIMER WITH THE FOLLOWING
	CHARACTERISTICS SHALL BE COATED CAREFULLY IN ORDER TO FULLY IMPREGNATE AND
	SATURATE THE COMPOUND.

	BASE	SILICON EPOXY
	DFT (DRY FILM THICKESS)	900 MICRONS COMBINED WITH L-200 TAPE
	DRING TIME	MIN 8 HOURS AT 25°C AND 60% OF MOISTURE
	GUIDANCE COVERAGE	0.5 KG/M2 (NET SURFACE)
	SPECIFIC GRAVITY	1.16 (25°C)
	NONVOLATILE COMPONENT	60 +/- 1% WT
	VISCOSITY	8.0 +/- 3 PS (25°C)
	APPLICATION	FRUSH OR ROLLER COATING

2.4	L-200 CEMENT (FILLING MASTIC) ;

	IN CASE OF FLANGE OR VALVE, L-200 CEMENT WITH THE BELOW CHARACTERISTICS SHALL BE
	FILLED UP IN ORDER APPLY TAPE WRAPPING SMOOTHLY ;

	BASE	SILICON
	SPECIFIC GRAVITY	1.98 (25°C)
	NONVOLATILE COMPONENT	100% BY WT

2.5	L-200 TOP COAT

	FINAL SUNLIGHT L-200 TOP COAT (COLOR GRAY)WITH THE BELOW CHARACTERISTICS SHALL BE
	COATED CAREFULLY WHEN FINISHING TAPE WRAPPING ;

	BASE	SILICON EPOXY
	DFT (DRY FILM THICKESS)	80 MICRONS
	DRING TIME	24 HOURS AT 25°C AND 60% OF MOISTURE NO CURING TIME REQUIRED
	GUIDANCE COVERAGE	0.68 KG/M2 (NET SURFACE)
	SPECIFIC GRAVITY	1.13 (25°C)
	NONVOLATILE COMPONENT	59 +/- 1% WT
	VISCOSITY	8.0 +/- 3 PS (25°C)

	TOTAL DFT = 1030 MICRONS

	NOTE 1 : EXCEPT FOR L-200 CEMENT, THE VALUES FOR NONVOLATILE COMPONENTS, VISCOSITY
	AND SPECIFIC GRAVITY MAY CHANGE DEPENDING UPON THE ENVIRONMENTAL CONDITIONS AT THE
	TIME OF APPLICATION.