CHARACTERISTICS

USES

Natural Ultra-fine Calcium Carbonate Powder manufactured from high-purity limestone by assembly-line:

HOSOKAWA-ALPINE – Germany technique

- Be popularly used in many industries namely: Paper, Paint, PVC compound or Master batches…etc as a functional filler or additive.

- Other applications

CHEMICAL  ANALYSIS  OF  THE  RAW  MATERIAL

COMPOUND

Calcium Carbonate – CaCO₃

Magnesium – MgO

Iron Oxide – Fe₂O₃

Aluminum Oxide – Al₂O₃

Silica – SiO₂

Natri Oxide - Na₂O

Method: TCN 09 -  I PTH/94 ; TCVN

VALUE

≥ 98 %

≤ 0.16 %

≤ 0.01 %

≤ 0.04 %

≤ 0.01 %

≤ 0.16 %

PHYSICAL PRROPERTIES OF RAW  MATERIAL

Hardness

Loss on Ignition

2.7 Moh

≤ 43.08 %

TECHNICAL DATA OF THE PRODUCED MATERIAL

Moisture

PH Value

DOP oil Absorption

Whiteness

Brightness

≤ 0.2 %

8 ÷ 9

24g / 100g CaCO₃ 

97 ± 1 %

94%

FINENESS (PARTICLE LASER DIFACTION MALVERN – ENGLAND)

Product code

Fineness

Mesh

GELE 05-MT

D50 (Particle Size)

D97 (Top cut)

1.4 ± 0.5 µm

05 ± 2.0 µm

2500 mesh

GELE 08-MT

D50 (Particle Size)

D97 (Top cut)

1.8 ± 0.5 µm

08 ± 2.0 µm

1880 mesh

C-GELE 08-MT

D50 (Particle Size)

D97 (Top cut)

Coated stearic acid ratio

1.8 ± 0.5 µm

08 ± 2.0 µm

1.15-1.25%

1880 mesh

GELE 10-MT

D50 (Particle Size)

D97 (Top cut)

2.5 ± 0.5 µm

10 ± 2.0 µm

1250 mesh

C-GELE 10-MT

D50 (Particle Size)

D97 (Top cut)

Coated stearic acid ratio

2.5 ± 0.5 µm

10 ± 2.0 µm

1.15-1.25%

1250 mesh

GELE 12-MT

D50 (Particle Size)

D97 (Top cut)

3.0 ± 0.5 µm

12 ± 2.0 µm

1100 mesh

C-GELE 12-MT

D50 (Particle Size)

D97 (Top cut)

Coated stearic acid ratio

3.0 ± 0.5 µm

12 ± 2.0 µm

1.15-1.25%

1100 mesh

GELE 15-TH

D50 (Particle Size)

D97 (Top cut)

4.4 ± 0.5 µm

15 ± 2.0 µm

800 mesh

C-GELE 15-MT

D50 (Particle Size)

D97 (Top cut)

Coated stearic acid ratio

4.0 ± 0.5 µm

15 ± 2.0 µm

1.15-1.25%

1000 mesh

GELE 17-TH

D50 (Particle Size)

D97 (Top cut)

4.8 ± 0.5 µm

17 ± 2.0 µm

700 mesh

GELE 20-TH

D50 (Particle Size)

D97 (Top cut)

5.3 ± 0.5 µm

20 ± 2.0 µm

625 mesh

C-GELE 20-MT

D50 (Particle Size)

D97 (Top cut)

Coated stearic acid ratio

5.0 ± 0.5 µm

20 ± 2.0 µm

1.15-1.25%

625 mesh

GELE 25-TH

D50 (Particle Size)

D97 (Top cut)

5.8 ± 0.5 µm

25 ± 1.0 µm

500 mesh

GELE 27-TH

D50 (Particle Size)

D97 (Top cut)

6.5 ± 0.5 µm

27 ± 2.0 µm

480 mesh

GELE 30-TH

D50 (Particle Size)

D97 (Top cut)

6.8 ± 0.5 µm

30 ± 2.0 µm

450 mesh

GELE 45-TH

D50 (Particle Size)

D97 (Top cut)

12 µm ± 0.5 µm

45 ± 2.0 µm

325 mesh

GELE 45-TH

D50 (Particle Size)

D97 (Top cut)

8.5 µm ± 0.5 µm

45 ± 2.0 µm

325 mesh

Particle size was measured by Malvern Mastersizer Hydro 2000MU – England

Other size can adjust particle sizes following the customer's requirements.

ORIGIN

Nghe An province, Vietnam

PACKING:

PP bag coated PE, 25kg